PARAMETRII CELULELOR SOLARE nITO/pInP OBŢINUTE PRIN METODA PULVERIZĂRII PIROLITICE ÎN DEPENDENŢĂ DE TRATAREA LOR TERMICĂ ÎN HIDROGEN: Alexei SIMAŞCHEVICI, Dormidont ŞERBAN, Leonid GORCEAC, Leonid BRUK, Andrei COVAL, Iurie USATII, Vladimir FEDOROV LCŞ „Fizica Semiconductorilor” ٭ Institutul de Fizică Aplicată al AŞM

USM ADMIN

PARAMETRII CELULELOR SOLARE nITO/pInP OBŢINUTE PRIN METODA PULVERIZĂRII PIROLITICE ÎN DEPENDENŢĂ DE TRATAREA LOR TERMICĂ ÎN HIDROGEN

Alexei SIMAŞCHEVICI, Dormidont ŞERBAN, Leonid GORCEAC, Leonid BRUK, Andrei COVAL, Iurie USATII, Vladimir FEDOROV LCŞ „Fizica Semiconductorilor” ٭ Institutul de Fizică Aplicată al AŞM

Autori

USM ADMIN Studia Universitas Moldaviae

Rezumat

The main objective of this communication is the investigation of the influence of thermal treatment in H2 on the parameters of In/nITO/P2O5/pInP/Ag:Zn solar cells obtained by ITO layers pyrolithic pulverization. The ITO/pInP heterostructures obtaining take place at the temperature of 450ºC. The photoelectric parameters of the solar cell received on InP wafers with concentration p = 3·1017cm-3 after the thermal treatment are Voc=0.626 V, Isc = 22.72 mA/cm2, FF = 71%, Eff = 10.09%. As a result of these investigations it was shown that the thermal treatment of In/nITO/pInP/Ag:Zn SC in H2 at 350oC during 10 min. leads to considerable improvement of their photoelectric parameters.